The C-Series family, a triacetate/diacetate blend, has a higher flux and better mechanical stability than standard cellulose acetate. CA-Series elements offer a lower per element cost and increased chlorine resistance compared to thin-film elements.

CE Brackish Water Elements are used for brackish water desalination and process stream concentration at 425 psig operating pressure (2,930 kPa).
Unit of Measure

Element Specification

Membrane

 N/A C-series, Cellulose Acetate

Flow Average

 N/A 630 gpd2.4 m³/day

Salt Rejection Average (NaCl)

 N/A 97.5 %

Salt Rejection Minimum (NaCl)

 N/A 95.0 %

Note

 N/A Average salt rejection after 24 hours operation. Individual flow rate may vary +25%/-15%.
Testing conditions: 2,000 ppm NaCl solution at 425 psig (2,930 kPa) operating pressure, 77ºF, pH 6.5 and 15% recovery.

Active Area

 N/A 27 ft²2.5 m²

Outer Wrap

 N/A Fiberglass

Part Number

 N/A 1206854

Dimensions and Weight

Dimension A (Length)

 N/A 40.0 in101.6 cm
Dimension B1 N/A 0.75 inOD: 1.90 cm

Dimension C (Outside Diameter)

 N/A 2.4 in6.1 cm

Boxed Weight

 N/A 5 lb2.3 kg

Operating and CIP parameters

Typical Operating Pressure

 N/A 140 - 400 psig965 - 2758 kPa

Typical Operating Flux

 N/A 10 - 18 GFD17 - 30 LMH

Maximum Pressure

 N/A 450 psig3103 kPa

Maximum Operating Temperature

 N/A 86 ºF30 ºC

Maximum Cleaning Temperature

 N/A 86 ºF30 ºC

Operating Range Recommended pH

N/A 5.0 - 6.5

Cleaning Range Recommended pH

N/A 3.0 - 8.0

Recommended Pressure Drop Over an Element

 N/A 12 psig83 kPa

Recommended Pressure Drop Per Housing

 N/A 50 psig345 kPa

Chlorine Tolerance

 N/A 1 ppm Maximum Continuous
30 ppm for 30 min. During Sanitization

Feedwater

 N/A NTU < 1 SDI < 5

Note

N/A These elements are shipped dry.
Trademark of General Electric Company; may be registered in one or more countries.