The C-Series family, a triacetate/diacetate blend, has a higher flux and better mechanical stability than standard cellulose acetate. C-Series elements offer a lower per element cost and increased chlorine resistance compared to thin-film elements.

CG High Flux Elements are used for brackish water desalination and process stream concentration at 225 psig (1,551 kPa) operating pressure.
Unit of Measure

Element Specification

Membrane

 N/A C-series, Cellulose Acetate

Flow Average

 N/A 7300 gpd27.6 m³/day

Salt Rejection Average (NaCl)

 N/A 93.0 %

Salt Rejection Minimum (NaCl)

 N/A 85.0 %

Note

 N/A Average salt rejection after 24 hours operation. Individual flow rate may vary +25%/-15%.
Testing conditions: 500 ppm NaCl solution at 210 psig (1,448 kPa) operating pressure, 77ºF, pH 6.5 and 15% recovery.

Active Area

 N/A 350 ft²32.5 m²

Outer Wrap

 N/A Fiberglass

Part Number

 N/A 1206896

Dimensions and Weight

Dimension A (Length)

 N/A 40.0 in101.6 cm
Dimension B1 N/A 1.125 in2.86 cm

Dimension C (Outside Diameter)

 N/A 7.9 in20.1 cm

Boxed Weight

 N/A 32 lb14.5 kg

Operating and CIP parameters

Typical Operating Pressure

 N/A 60 - 200 psig414 - 1379 kPa

Typical Operating Flux

 N/A 10 - 18 GFD17 - 30 LMH

Maximum Pressure

 N/A 450 psig3103 kPa

Maximum Operating Temperature

 N/A 86 ºF30 ºC

Maximum Cleaning Temperature

 N/A 86 ºF30 ºC

Operating Range Recommended pH

N/A 5.0 - 6.5

Cleaning Range Recommended pH

N/A 3.0 - 8.0

Recommended Pressure Drop Over an Element

 N/A 12 psig83 kPa

Recommended Pressure Drop Per Housing

 N/A 50 psig345 kPa

Chlorine Tolerance

 N/A 1 ppm Maximum Continuous
30 ppm for 30 min. During Sanitization

Feedwater

 N/A NTU < 1 SDI < 5

Note

N/A These elements are shipped dry.